Optimization of Process Parameters to Minimize the Surface Roughness of Abrasive Water Jet Machined Jute/Epoxy Composites for Different Fiber Inclinations

Document Type

Article

Publication Title

Journal of Composites Science

Abstract

Composites materials like jute/epoxy exhibit high hardness and are considered as difficult-to-machine materials. As a result, alternatives to conventional machining become essential to post-process the composites. Accordingly, due to its non-thermal nature, abrasive water jet machining has recently come to be seen as one of the most promising machining methods for composite materials. In the current study, the impact of machining parameters such as traverse speed (TS), standoff distance (SOD) and abrasive mass flow rate (MFR) on machined surface roughness (Ra) has been investigated. In addition, the optimum combination of process parameters to machine a jute fiber-reinforced polymer composite with minimum Ra is predicted. The experimental results are analyzed using Taguchi and Response Surface Methodology (RSM) approaches to determine the optimum set of process parameters to achieve the lowest roughness values. Without making any changes in the machining conditions, the optimum set of values is determined for two conditions by reinforcing the fiber with 45° inclination and 90° inclination. The results reflect the different optimum combinations for each fiber inclination. For 45° fiber inclination, to achieve the minimum Ra value, the predicted combination is TS = 30 mm/min, SOD = 2 mm and MFR = 0.35 kg/min. When the fiber inclination is 90°, the predicted optimum combination is TS = 25 mm/min, SOD = 2 mm, and MFR = 0.35 kg/min. It is evident from the results that the optimum combination will be changed according to the machining conditions as well as material properties. The results confirm the effect of fiber orientation on surface roughness. The specimen with 45° fiber inclination produces a lower Ra with an average of 4.116 µm, and the specimen with 90° fiber inclination generates a higher Ra with an average of 4.961 µm.

DOI

10.3390/jcs7120498

Publication Date

12-1-2023

This document is currently not available here.

Share

COinS