Experimental Investigation of Mechanical Property and Wear Behaviour of T6 Treated A356 Alloy with Minor Addition of Copper and Zinc

Document Type

Article

Publication Title

Journal of Composites Science

Abstract

The present study examines the effect of trace additions of copper (up to 1 wt.%) and zinc (0.5 wt.%) as the alloying elements on the microstructure, hardness, and wear behaviour of T6 treated A356 (Al-7Si) alloy. Wear tests were conducted using a pin-on-disc tribometer under a constant sliding speed of 200 RPM, varying applied load (20–40 N), and sliding distance (0–3000 m) to determine the wear rate and the coefficient of friction. The results indicated a minimum of 1 wt.% of copper was required to form the Al2Cu intermetallic phase, resulting in a finer grain structure and improved hardness. However, the role of zinc as a trace element was not observed on the microstructure; the observed changes may be the combined effect of copper and zinc as a whole. The highest hardness of 107 VHN (98% increase) was achieved with 1 wt.% copper addition during peak aging at 100 °C. Also, wear tests showed that adding 1 wt.% copper to the A356 alloy and a 100 °C precipitation hardening (T6) treatment improved the wear resistance by 150–182% with a reduced coefficient of friction.

DOI

10.3390/jcs7040149

Publication Date

4-1-2023

This document is currently not available here.

Share

COinS